FinFET semiconductor device with a recessed liner that defines a fin height of the FinFet device

ABSTRACT

One method disclosed herein includes forming a conformal liner layer in a plurality of trenches that define a fin, forming a layer of insulating material above the liner layer, exposing portions of the liner layer, removing portions of the liner layer so as to result in a generally U-shaped liner positioned at a bottom of each of the trenches, performing at least one third etching process on the layer of insulating material, wherein at least a portion of the layer of insulating material is positioned within a cavity of the U-shaped liner layer, and forming a gate structure around the fin. A FinFET device disclosed herein includes a plurality of trenches that define a fin, a local isolation that includes a generally U-shaped liner that defines, in part, a cavity and a layer of insulating material positioned within the cavity, and a gate structure positioned around the fin.

CROSS-REFERENCE TO RELATED APPLICATION

This is a divisional of co-pending application Ser. No. 13/711,813,filed Dec. 12, 2012.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Generally, the present disclosure relates to the manufacture ofsophisticated semiconductor devices, and, more specifically, to variousmethods of forming 3D semiconductor devices, such as FinFET devices, byperforming a liner recessing process to define the fin height of theFinFET device, and to a FinFET device that includes such a recessedliner structure.

2. Description of the Related Art

The fabrication of advanced integrated circuits, such as CPU's, storagedevices, ASIC's (application specific integrated circuits) and the like,requires the formation of a large number of circuit elements in a givenchip area according to a specified circuit layout, wherein so-calledmetal oxide field effect transistors (MOSFETs or FETs) represent oneimportant type of circuit element that substantially determinesperformance of the integrated circuits. A FET is a planar device thattypically includes a source region, a drain region, a channel regionthat is positioned between the source region and the drain region, and agate electrode positioned above the channel region. Current flow throughthe FET is controlled by controlling the voltage applied to the gateelectrode. If there is no voltage applied to the gate electrode, thenthere is no current flow through the device (ignoring undesirableleakage currents, which are relatively small). However, when anappropriate voltage is applied to the gate electrode, the channel regionbecomes conductive, and electrical current is permitted to flow betweenthe source region and the drain region through the conductive channelregion.

To improve the operating speed of FETs, and to increase the density ofFETs on an integrated circuit device, device designers have greatlyreduced the physical size of FETs over the years. More specifically, thechannel length of FETs has been significantly decreased, which hasresulted in improving the switching speed of FETs. However, decreasingthe channel length of a FET also decreases the distance between thesource region and the drain region. In some cases, this decrease in theseparation between the source and the drain makes it difficult toefficiently inhibit the electrical potential of the source region andthe channel from being adversely affected by the electrical potential ofthe drain. This is sometimes referred to as a so-called short channeleffect, wherein the characteristic of the FET as an active switch isdegraded.

In contrast to a FET, which has a planar structure, a so-called FinFETdevice has a three-dimensional (3D) structure. More specifically, in aFinFET, a generally vertically positioned fin-shaped active area isformed and a gate electrode encloses both sides and an upper surface ofthe fin-shaped active area to form a tri-gate structure so as to use achannel having a three-dimensional structure instead of a planarstructure. In some cases, an insulating cap layer, e.g., siliconnitride, is positioned at the top of the fin and the FinFET device onlyhas a dual-gate structure. Unlike a planar FET, in a FinFET device, achannel is formed perpendicular to a surface of the semiconductingsubstrate so as to reduce the physical size of the semiconductor device.Also, in a FinFET, the junction capacitance at the drain region of thedevice is greatly reduced, which tends to reduce at least some shortchannel effects. When an appropriate voltage is applied to the gateelectrode of a FinFET device, the surfaces (and the inner portion nearthe surface) of the fins, i.e., the substantially vertically orientedsidewalls and the top upper surface of the fin with inversion carriers,contributes to current conduction. In a FinFET device, the“channel-width” is approximately two times (2×) the vertical fin-heightplus the width of the top surface of the fin, i.e., the fin width.Multiple fins can be formed in the same foot-print as that of a planartransistor device. Accordingly, for a given plot space (or foot-print),FinFETs tend to be able to generate significantly stronger drivecurrents than planar transistor devices. Additionally, the leakagecurrent of FinFET devices after the device is turned “OFF” issignificantly reduced as compared to the leakage current of planar FETsdue to the superior gate electrostatic control of the “fin” channel onFinFET devices. In short, the 3D structure of a FinFET device is asuperior MOSFET structure as compared to that of a planar FET,especially in the 20 nm CMOS technology node and beyond.

One process flow that is typically performed to form FinFET devicesinvolves forming a plurality of trenches in the substrate to define theareas where STI regions will be formed and to define the initialstructure of the fins. These trenches are typically formed in thesubstrate during the same process operation for processing simplicity.The trenches have a target depth that is sufficient for the needed finheight and deep enough to allow formation of an effective STI region.After the trenches are formed, a layer of insulating material, such assilicon dioxide, is formed so as to overfill the trenches. Thereafter, achemical mechanical polishing (CMP) process is then performed toplanarize the upper surface of the insulating material with the top ofthe fins (or the top of a patterned hard mask). Thereafter, an etch-backprocess is performed to recess the layer of insulating material betweenthe fins and thereby expose the upper portions of the fins, whichcorresponds to the final fin height of the fins.

Some integrated circuit products contain FinFET devices that have adifferent fin pitch, i.e., different fin spacing. FIG. 1A schematicallydepicts an illustrative prior art integrated circuit product 10 at apoint of fabrication wherein a plurality of trenches 12 have been formedin a bulk semiconducting substrate 14 by performing an etching processthrough a patterned hard mask layer 16, e.g., a patterned layer ofsilicon dioxide. The etching process results in the formation of aplurality of fins 20. The product 10 comprises a region 20N where theFinFET devices have fins with a relatively narrow fin pitch 22N, e.g.,20-50 nm, and another region 20W where the FinFET devices have fins witha relatively wide fin pitch 22W, e.g., 1 μm or more. These regions aretypically spaced apart on the substrate 14.

FIG. 1B depicts the product 10 after the patterned hard mask layer 16has been removed, a layer of insulating material 24, e.g., silicondioxide, has been deposited so as to overfill the trenches and a CMPprocess has been performed on the layer of insulating material in aneffort to planarize the upper surface of the layer of insulatingmaterial 24 with the upper surface of the fins 20. As a result of therelatively wider fin pitch in the area 20W, there may be more dishing 26in the region 20W than in the region 20N having the narrower fin pitch.

FIG. 1C depicts the prior art product 10 at a point in fabricationwherein a timed etching process has been performed on the layer ofinsulating material 24 to reduce its thickness and thereby define areduced-thickness layer of insulating material 24R. Typically,semiconductor manufacturers try to establish the final height of thefins for the FinFET devices by controlling this etching process and theresulting thickness of the reduced-thickness layer of insulatingmaterial 24R.

There are several problems with the aforementioned process of formingfins for FinFET semiconductor devices. More specifically, as depicted inFIG. 1C, such a process flow may produce fins with varying heights 28A,28B and 28C across the substrate. Such variations in fin height areundesirable from a design, manufacturing and performance standpoint. Forexample, if the fin height on a FinFET device is less than the targetfin height determined by the design process, the resulting FinFET devicemay not produce as large of drive current as is anticipated by thecircuit designer and the circuit may not function as well asanticipated. Having fins with differing height levels can also makemanufacturing more difficult in that it becomes more difficult toachieve a planar surface in subsequent processing operations.

Such differences in fin height may be the result, at least in part, ofseveral factors. Since the etching process that is performed to recessthe layer of insulating material 24R (see FIG. 1C) is a timed etchingprocess, there are variations in the resulting thickness of thereduced-thickness layer of insulating material 24R. Another factor thatcontributes to this undesirable situation may be excessive dishing 26 ofthe layer of insulating material 24 during the CMP process depicted inFIG. 1B. As a result of such dishing 26, after the recess etch processis performed, the fins in areas where such dishing is present may have afin height that is greater than the target fin height due to thereduction in thickness of the layer of insulating material 24 as aresult of the excessive dishing. Additionally, the initial depth of thetrenches 12 in the region 20N may be different than the depth of thetrenches 12 in the region 20W due to the difference in fin pitch inthose two regions.

Device manufacturers are under constant pressure to produce integratedcircuit products with increased performance and lower production costrelative to previous device generations. Thus, device designers spend agreat amount of time in an effort to maximize device performance whileseeking ways to reduce manufacturing cost and improve manufacturingreliability. As it relates to 3D devices, device designers have spentmany years and employed a variety of techniques in an effort to improvethe performance capability and reliability of such devices.

The present disclosure is directed to various methods of forming 3Dsemiconductor devices, such as FinFET devices, by performing a linerrecessing process to define the fin height of the FinFET devices, and toa FinFET device that includes such a recessed liner structure, that maysolve or reduce one or more of the problems identified above.

SUMMARY OF THE INVENTION

The following presents a simplified summary of the invention in order toprovide a basic understanding of some aspects of the invention. Thissummary is not an exhaustive overview of the invention. It is notintended to identify key or critical elements of the invention or todelineate the scope of the invention. Its sole purpose is to presentsome concepts in a simplified form as a prelude to the more detaileddescription that is discussed later.

Generally, the present disclosure is directed to various methods offorming 3D semiconductor devices, such as FinFET devices, by performinga liner recessing process to define the fin height of the FinFET device,and to a FinFET device that includes such a recessed liner structure. Inone example, the method disclosed herein includes performing at leastone first etching process through a patterned hard mask layer to form aplurality of trenches in a semiconducting substrate so as to therebydefine a fin, forming a conformal liner layer above the hard mask and inthe trenches, forming a layer of insulating material in the trenchesabove the liner layer and removing portions of the layer of insulatingmaterial so as to expose portions of the liner layer. The method alsoincludes performing at least one second etching process to removeportions of the liner layer and the hard mask layer, wherein the etchingprocess results in a generally U-shaped liner positioned at a bottom ofeach of the trenches, performing at least one third etching process onthe layer of insulating material to thereby define a reduced-thicknesslayer of insulating material, wherein at least a portion of the reducedthickness layer of insulating material is positioned within a cavitydefined by the generally U-shaped liner layer, and forming a gatestructure around a portion of said fin.

Another illustrative method disclosed herein for forming a FinFET devicehaving a target final fin height includes forming a patterned hard masklayer above a semiconducting substrate, performing at least one firstetching process through the patterned hard mask layer to form aplurality of trenches in the substrate, wherein the trenches define afin, selecting, based upon the target final fin height, a targetthickness for a conformal liner layer to be formed above the patternedhard mask layer and in the trenches and forming the conformal linerlayer having the target thickness above the patterned hard mask layerand in the trenches. The method further includes forming a layer ofinsulating material in the trenches above the conformal liner layer,performing a process operation to remove portions of the layer ofinsulating material and to expose portions of the conformal liner layer,performing at least one second etching process to remove portions of theconformal liner layer and the patterned hard mask layer, wherein theetching process results in a generally U-shaped liner positioned at abottom of each of the trenches and wherein the substantially U-shapedliner exposes a portion of the fin that corresponds to the final desiredfin height, performing at least one third etching process on the layerof insulating material to thereby define a reduced-thickness layer ofinsulating material and forming a gate structure around a portion of thefin having the final desired fin height.

One illustrative FinFET device disclosed herein includes a plurality oftrenches formed in a semiconducting substrate that define a fin, a localisolation region positioned in a bottom of each of the trenches, whereinthe local isolation region includes a generally U-shaped liner that hasa plurality of spaced apart generally upstanding vertically orientedlegs that define, in part, a cavity and a layer of insulating materialpositioned within the cavity in the generally U-shaped liner, and a gatestructure positioned around a portion of the fin.

BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure may be understood by reference to the followingdescription taken in conjunction with the accompanying drawings, inwhich like reference numerals identify like elements, and in which:

FIGS. 1A-1C depict one illustrative prior art method of forming fins fora FinFET device; and

FIGS. 2A-2I depict various illustrative methods of forming anillustrative FinFET device by performing a liner recessing process todefine the fin height of the FinFET device and the resulting device.

While the subject matter disclosed herein is susceptible to variousmodifications and alternative forms, specific embodiments thereof havebeen shown by way of example in the drawings and are herein described indetail. It should be understood, however, that the description herein ofspecific embodiments is not intended to limit the invention to theparticular forms disclosed, but on the contrary, the intention is tocover all modifications, equivalents, and alternatives falling withinthe spirit and scope of the invention as defined by the appended claims.

DETAILED DESCRIPTION

Various illustrative embodiments of the invention are described below.In the interest of clarity, not all features of an actual implementationare described in this specification. It will of course be appreciatedthat in the development of any such actual embodiment, numerousimplementation-specific decisions must be made to achieve thedevelopers' specific goals, such as compliance with system-related andbusiness-related constraints, which will vary from one implementation toanother. Moreover, it will be appreciated that such a development effortmight be complex and time-consuming, but would nevertheless be a routineundertaking for those of ordinary skill in the art having the benefit ofthis disclosure.

The present subject matter will now be described with reference to theattached figures. Various structures, systems and devices areschematically depicted in the drawings for purposes of explanation onlyand so as to not obscure the present disclosure with details that arewell known to those skilled in the art. Nevertheless, the attacheddrawings are included to describe and explain illustrative examples ofthe present disclosure. The words and phrases used herein should beunderstood and interpreted to have a meaning consistent with theunderstanding of those words and phrases by those skilled in therelevant art. No special definition of a term or phrase, i.e., adefinition that is different from the ordinary and customary meaning asunderstood by those skilled in the art, is intended to be implied byconsistent usage of the term or phrase herein. To the extent that a termor phrase is intended to have a special meaning, i.e., a meaning otherthan that understood by skilled artisans, such a special definition willbe expressly set forth in the specification in a definitional mannerthat directly and unequivocally provides the special definition for theterm or phrase.

In general, the present disclosure is directed to various methods offorming 3D semiconductor devices, such as FinFET devices, by performinga liner recessing process to define the fin height of the FinFET device,and to a FinFET device that includes such a recessed liner structure.Moreover, as will be readily apparent to those skilled in the art upon acomplete reading of the present application, the present method isapplicable to a variety of devices, including, but not limited to, logicdevices, memory devices, etc., and the methods disclosed herein may beemployed to form N-type or P-type semiconductor devices. With referenceto the attached figures, various illustrative embodiments of the methodsand devices disclosed herein will now be described in more detail.

The point of fabrication depicted in FIG. 2A for the novel integratedcircuit product 100 disclosed herein corresponds approximately to thepoint of fabrication depicted in FIG. 1A for the prior art product 10.FIGS. 2A-2I make use of some of the same reference numbers as previouslydiscussed with respect to FIGS. 1A-1C and those numbers should beunderstood to refer to the same general structure as previouslydescribed, as supplemented herein.

FIG. 2A schematically depicts the novel integrated circuit product 100at a point of fabrication wherein a plurality of trenches 12 have beenformed in a bulk semiconducting substrate 14 by performing at least oneetching process through a patterned hard mask layer 16, e.g., apatterned layer of silicon nitride. The etching process results in theformation of a plurality of fins 20. The product 100 comprises a region20N where the FinFET devices have fins with a relatively narrow finpitch 22N, e.g., 20-30 nm, and another region 20W where the FinFETdevices have fins with a relatively wide fin pitch 22W, e.g., 1 μm ormore. The regions 22N, 22W are typically spaced apart on the substrate14 and each region may contain thousands (or more) of individual FinFETdevices. However, as will be recognized by those skilled in the artafter a complete reading of the present application, the inventionsdisclosed herein may be applied to the formation of a single FinFETdevice irrespective of whether or not the integrated circuit product 100contains additional FinFET devices having a different fin pitch. Thus,the illustrative example of the product 100 having FinFET devices withdifferent fin pitches should not be considered to be a limitation of thepresent invention.

The substrate 14 may have a variety of configurations, such as thedepicted bulk substrate configuration. The substrate 14 may be made ofsilicon or it may be made of materials other than silicon. Thus, theterms “substrate” or “semiconducting substrate” should be understood tocover all semiconducting materials and all forms of such materials.Additionally, the overall size, shape and configuration of the trenches12 and fins 20 may vary depending on the particular application. Thedepth and width of the trenches 12 may also vary depending upon theparticular application. In one illustrative embodiment, based on currentday technology, the depth of the trenches 12 may range fromapproximately 30-200 nm and the width of the trenches 12 may range fromabout 20-50 nm. In some embodiments, the fins 20 may have a width withinthe range of about 5-30 nm. In the illustrative examples depicted inmost of the attached drawings, the trenches 12 and fins 20 are all of auniform size and shape. However, as discussed more fully below, suchuniformity in the size and shape of the trenches 12 and the fins 20 isnot required to practice at least some aspects of the inventionsdisclosed herein. In most of the attached figures, the trenches 12 areformed by performing an anisotropic etching process that results in thetrenches 12 having a schematically depicted, generally rectangularconfiguration. In an actual real-world device, the sidewalls of thetrenches 12 may be somewhat inwardly tapered, although thatconfiguration is not depicted in most of the attached drawings. In somecases, the trenches 12 may have a reentrant profile near the bottom ofthe trenches 12. To the extent the trenches 12 are formed by performinga wet etching process, the trenches 12 may tend to have a more roundedconfiguration or non-linear configuration as compared to the generallyrectangular configuration of the trenches 12 that are formed byperforming an anisotropic etching process. Thus, the size andconfiguration of the trenches 12, and the manner in which they are made,as well as the general configuration of the fins 20, should not beconsidered a limitation of the present invention. For ease ofdisclosure, only the substantially rectangular trenches 12 will bedepicted in most of the subsequent drawings.

FIG. 2B depicts the product 100 after a conformal deposition process,e.g., a chemical vapor deposition (CVD) process, an atomic layerdeposition (ALD) process, etc., has been performed to form a liner 102on the product 100. More specifically, in the depicted example, theliner 102 is formed above the patterned hard mask layer 16, on thesidewalls of the fins 20 and in the trenches 12. The thickness 102T ofthe liner 102 may vary depending upon the particular application, e.g.,it may have a thickness of about 5-10 nm. As described more fully below,using the processes described herein, the fin height of the fins of theFinFET devices are set by selecting the desired thickness 102T of theliner 102. In general, the liner 102 may be made of a material that maybe selectively etched relative to the insulating material that will beused to fill the remaining portions of the trenches 12. For example, theliner 102 may be comprised of silicon nitride, silicon carbon nitride,silicon boron nitride, a doped nitride, silicon oxynitride, etc. In oneparticularly illustrative embodiment, both the patterned hard mask layer16 and the liner 102 may be made of silicon nitride.

FIG. 2C depicts the product 100 after a layer of insulating material 104has been deposited so as to overfill the trenches 12 and after a CMPprocess has been performed on the layer of insulating material 104 in aneffort to planarize the upper surface 104S of the layer of insulatingmaterial 104. In the depicted example, the CMP process stops on theliner 102. As discussed previously, as a result of the relatively widerfin pitch in the area 20W, there may be more undesirable dishing 106 inthe region 20W than in the region 20N having the narrower fin pitch. Thelayer of insulating material 104 may be comprised of a variety ofdifferent materials, such as silicon dioxide, doped silicon dioxide(doped with carbon, boron or phosphorous), etc., and it may be formed byperforming a variety of techniques, e.g., chemical vapor deposition(CVD), etc. Instead of a CMP process, an etch-back process could beperformed on the layer of insulating material 104 to arrive atsubstantially the same structure as depicted in FIG. 2C.

FIGS. 2D-2E show the product 100 after an etching sequence has beenperformed on the product 100 to recess the liner 102 within the trenches12. Initially, if desired, an optional oxide deglaze etching process maybe performed to insure that all of the insulating material 104, e.g.,silicon dioxide, is removed from the upper surfaces of the liner 102.Thereafter, an etching process is performed to remove the patterned hardmask 16 and the liner 102 selectively relative to the insulatingmaterial 104. FIG. 2D depicts the product 100 at the point where theetching process has removed portions of the liner 102 and the patternedhard mask 16. The reference number 102X is used to depict the liner 102at this point in the recess etching process. FIG. 2E depicts the product100 at the end of the etching process wherein the liner 102 has beenrecessed sufficiently to establish the final exposed fin height 20F ofthe fins 20. The reference number 102Y is used to depict the liner 102at this point in the recess etching process.

In general, the etch rate in the above-described liner recess etchprocess decreases the further (or deeper) the liner 102 is recessed,which provides a means to effectively control the depth of the linerrecess. The slowing of the etch process in such a narrow space occupiedby the vertically oriented portions of the liner 102 may be referred toas a so-called capillary effect. It should also be noted that thecontrol of the fin height 20F is not dependent upon the fin pitch indifferent regions of the product, since the thickness 102T of the liner102 is the same in all regions, irrespective of fin pitch. Thus, theliner 102 may be recessed to the same depth across the product 100,which results in a substantially uniform fin height 20F across theproduct 100. In general, the greater the thickness 102T of the conformalliner 102, the greater will be the resulting substantially uniform finheight 20F across the substrate. Stated another way, increasing thethickness 102T of the liner 102 means that the cavity 102C above theliner 102 during the recess etch process is wider, which does not slowthe etch rate of the recess etch process as much as a narrower cavity102C that results from the use of a thinner liner 102. By selecting theappropriate target thickness 102T (either a specific number or a range)of the liner 102, the target final fin height 20F for all fins acrossthe substrate and within a particular FinFET device may be set andcontrolled using the methods disclosed herein. For example, using themethods disclosed herein, setting the target thickness 102T of the liner102 at values A, B and C results in a product 100 having a substantiallyuniform final fin height 20F of X, Y and Z, respectively, across thesubstrate. The relationship between the liner thickness 102T and thefinal fin height 20F may vary depending upon a variety of factors, e.g.,the materials used for the liner 102, the etchants used in the recessetch process, the geometry of the trench 12, etc. Moreover, therelationship between the liner thickness 102T and the final fin height20F may not be linear. Accordingly, it is anticipated that, inimplementing the present inventions, testing may be required toestablish the exact parameters of, for example, liner material, linerthickness and etching process conditions and materials to arrive at asolution tailored for a particular product 100.

FIG. 2F depicts the product 100 at a point in fabrication wherein atimed etching process has been performed on the layer of insulatingmaterial 104 to reduce its thickness and thereby define areduced-thickness layer of insulating material 104R. This processresults in the formation of local isolation regions 107 in the bottom ofthe trenches 12. The local isolation region 107 is generally comprisedof a generally “U” shaped liner 102Y with a pair of spaced-apartsubstantially upstanding or vertical leg portions 103 that are connectedby a substantially horizontal portion of the liner 102Y, and a portionof the layer of insulating material 104R positioned in the cavity 103Cdefined, in part, by the upstanding leg portions 103 of the liner 102Y.The same basic structure of the local isolation region 107 is present inboth of the regions 20N and 20W.

FIG. 2G is a depiction of a single FinFET device 101 that may be formedusing the methods disclosed herein. An illustrative device isolationregion 105, e.g., a shallow trench isolation region, is formed in thesubstrate 14 using traditional techniques. The device 101 includes aplurality of fins 20 having a final fin height 20F, a plurality oftrenches having local isolation regions 107 formed therein and a finalgate structure 110 comprised of an illustrative gate insulation layer110A and an illustrative gate electrode 110B. The final gate structure110 may be formed using so-called “gate-first” or “replacement-gate”(“gate-last”) techniques. An illustrative gate cap layer (not shown) mayalso be formed above the illustrative gate electrode 110B. The gateinsulation layer 110A may be comprised of a variety of differentmaterials, such as, for example, silicon dioxide, a so-called high-k (kgreater than 10) insulation material (where k is the relative dielectricconstant), etc. The thickness of the gate insulation layer 110A may alsovary depending upon the particular application, e.g., it may have athickness of about 1-2 nm. Similarly, the gate electrode 110B may alsobe of a variety of conductive materials, such as polysilicon oramorphous silicon, or it may be comprised of one or more metal layersthat act as the gate electrode 110B. As will be recognized by thoseskilled in the art after a complete reading of the present application,the gate structure 110 of the device 101 depicted in the drawings, i.e.,the gate insulation layer 110A and the gate electrode 110B, is intendedto be representative in nature. That is, the gate structure 110 may becomprised of a variety of different materials and it may have a varietyof configurations. In one illustrative embodiment, a thermal oxidationprocess may be performed to form the depicted gate insulation layer 110Acomprised of silicon dioxide. Thereafter, the gate electrode material110B and the gate cap layer material (not shown) may be deposited abovethe device 101 and the layers may be patterned using knownphotolithographic and etching techniques. In another illustrativeembodiment, a conformal CVD or ALD process may be performed to form agate insulation layer 110A comprised of hafnium oxide. Thereafter, oneor more metal layers (that will become the gate electrode 110B) and agate cap layer material (not shown), e.g., silicon nitride, may bedeposited above the device 101. At this point, traditional manufacturingtechniques may be performed to complete the manufacture of the device101. For example, sidewall spacers (not shown) comprised of, forexample, silicon nitride, may be formed adjacent the final gatestructure 110. After the spacers are formed, if desired, an epitaxialgrowth process may be performed to form additional semiconductingmaterial (not shown) on the portions of the fins 20 positioned outsideof the spacers. Additional contacts and metallization layers may then beformed above the device using traditional techniques.

FIGS. 2H and 2I provide illustrative examples where the trenches 12 havea more tapered or more rounded configuration, respectively.Nevertheless, a generally U-shaped local isolation region 107 is formedin the bottom of the devices with such variations in the configurationof the bottom portions of the trenches. In both of the situationsdepicted in FIGS. 2H-2I, the local isolation region 107 is generallycomprised of a generally “U” shaped liner 102Y with substantiallyupstanding or vertical leg portions 103 that are connected by ahorizontal portion of the liner 102Y, and a portion of the layer ofinsulating material 104R positioned in the cavity 103C defined, in part,by the upstanding leg portions 103 of the liner 102Y.

The particular embodiments disclosed above are illustrative only, as theinvention may be modified and practiced in different but equivalentmanners apparent to those skilled in the art having the benefit of theteachings herein. For example, the process steps set forth above may beperformed in a different order. Furthermore, no limitations are intendedto the details of construction or design herein shown, other than asdescribed in the claims below. It is therefore evident that theparticular embodiments disclosed above may be altered or modified andall such variations are considered within the scope and spirit of theinvention. Accordingly, the protection sought herein is as set forth inthe claims below.

What is claimed:
 1. An integrated circuit product device, comprising; afirst FinFET device formed in and above a first region of asemiconductor substrate, said first FinFET device comprising: aplurality of first fins separated by a first trench formed in saidsemiconductor substrate, said plurality of first fins having a first finpitch and a first fin height; and a first gate structure formed abovesaid plurality of first fins; a second FinFET device formed in and abovea second region of said semiconductor substrate, said second FinFETdevice comprising: a plurality of second fins separated by a secondtrench formed in said semiconductor substrate, said plurality of secondfins having a second fin pitch that is greater than said first fin pitchand a second fin height that is the same as said first fin height; and asecond gate structure formed above said plurality of second fins; and alocal isolation region positioned in a bottom of each of said first andsecond trenches, said local isolation region comprising: a U-shapedliner having a plurality of spaced-apart upstanding vertically orientedlegs that define, in part, a cavity, wherein said U-shaped liner definessaid first and second fin heights; and a layer of insulating materialpositioned within said cavity in said U-shaped liner, wherein said layerof insulating material in said first trench has a first substantiallyuniform height along an entire axial length of said first trench in adirection corresponding to a gate length direction of said first FinFETdevice, and said layer of insulating material in said second trench hasa second substantially uniform height along an entire axial length ofsaid second trench in a direction corresponding to a gate lengthdirection of said second FinFET device, wherein said first substantiallyuniform height in a center region of said first trench is greater thansaid second substantially uniform height in a center region of saidsecond trench.
 2. The device of claim 1, wherein said semiconductingsubstrate is comprised of silicon.
 3. The device of claim 1, whereinsaid layer of insulating material is positioned entirely within saidcavity in said U-shaped liner.
 4. The device of claim 1, wherein saidfirst and second gate structures are each comprised of a silicon dioxidegate insulation layer and a polysilicon gate electrode positioned abovesaid gate insulation layer.
 5. The device of claim 1, wherein said firstand second gate structures are each comprised of a gate insulation layercomprising a high-k insulating material and a gate electrode comprisingat least one layer of metal.
 6. The device of claim 1, wherein saidfirst and second trenches have at least one of vertical sidewalls,sloped sidewalls or curved sidewalls.
 7. The device of claim 1, whereinsaid first and second gate structures are each comprised of a gateinsulation layer and a polysilicon gate electrode positioned above saidgate insulation layer, and wherein said U-shaped liner has a firstthickness of between 5 and 10 nm and said gate insulation layer has asecond thickness less than said first thickness of said U-shaped liner.8. An integrated circuit product device, comprising; a first FinFETdevice formed in and above a first region of a semiconductor substrate,said first FinFET device comprising: a plurality of first fins separatedby a first trench formed in said semiconductor substrate, wherein saidfirst trench has sloped sidewall portions and said plurality of firstfins have a first fin pitch and a first fin height; and a first gatestructure formed above said plurality of first fins; a second FinFETdevice formed in and above a second region of said semiconductorsubstrate, said second FinFET device comprising: a plurality of secondfins separated by a second trench formed in said semiconductorsubstrate, wherein said second trench has sloped sidewall portions andsaid plurality of second fins have a second fin pitch that is greaterthan said first fin pitch and a second fin height that is the same assaid first fin height; and a second gate structure formed above saidplurality of second fins; and a local isolation region positioned in abottom of each of said first and second trenches, said local isolationregion comprising: a U-shaped liner having a plurality of spaced-apartupstanding legs positioned adjacent said sloped sidewall portions thatdefine, in part, a cavity, wherein said U-shaped liner defines saidfirst and second fin heights; and a layer of insulating materialpositioned within said cavity in said U-shaped liner, wherein said layerof insulating material in said first trench has a first substantiallyuniform height along an entire axial length of said first trench in adirection corresponding to a gate length direction of said first FinFETdevice, and said layer of insulating material in said second trench hasa second substantially uniform height along an entire axial length ofsaid second trench in a direction corresponding to a gate lengthdirection of said second FinFET device, wherein said first substantiallyuniform height in a center region of said first trench is greater thansaid second substantially uniform height in a center region of saidsecond trench.
 9. The device of claim 8, wherein said semiconductingsubstrate is comprised of silicon.
 10. The device of claim 8, whereinsaid layer of insulating material is positioned entirely within saidcavity in said U-shaped liner.
 11. The device of claim 8, wherein saidfirst and second gate structures are each comprised of a silicon dioxidegate insulation layer and a polysilicon gate electrode positioned abovesaid gate insulation layer.
 12. The device of claim 8, wherein saidfirst and second gate structures are each comprised of a gate insulationlayer comprising a high-k insulating material and a gate electrodecomprising at least one layer of metal.
 13. The device of claim 8,wherein said first and second gate structures are each comprised of agate insulation layer and a polysilicon gate electrode positioned abovesaid gate insulation layer, and wherein said U-shaped liner has a firstthickness of between 5 and 10 nm and said gate insulation layer has asecond thickness less than said first thickness of said U-shaped liner.14. The device of claim 1, wherein said first substantially uniformheight in an edge region of said first trench is substantially equal tosaid second substantially uniform height in an edge region of saidsecond trench.
 15. The device of claim 8, wherein said firstsubstantially uniform height in an edge region of said first trench issubstantially equal to said second substantially uniform height in anedge region of said second trench.